Transparent and antistatic pmma composition

ABSTRACT

A transparent antistatic composition based on polymethyl methacrylate (PMMA), including: 55% to 99.9% by weight of PMMA, and 0.1% to 45% by weight of at least one polyamide (PA) block-containing and polyether (PE) block-containing copolymer (PEBA) including polyethylene glycol (PEG), with respect to the total composition weight, said copolymer including in the range 50% to 80% by weight of PEG with respect to the total weight of copolymer. Also, the use of a composition of this type for the manufacture of at least a portion of the following items: an industrial part, an automobile part, a safety accessory, sign, luminous strip, signalling and advertizing panel, display, etching, furniture, shop fitting, decoration, contact ball, dental prosthesis, ophthalmological implant, membrane for hemodialysis, optic fibers, artwork, sculpture, camera lenses, disposable camera lenses, printing support, in particular a support for direct printing with UV inks for pictures, photographs, window glass, panoramic roof.

FIELD OF THE INVENTION

The present invention relates to a transparent antistatic composition based on polymethyl methacrylate (PMMA).

In the context of the invention:

-   -   “composition based on polymethyl methacrylate (PMMA)” means a         composition comprising 55% to 99.9% by weight of PMMA;     -   “transparent composition” means a composition with a         transmittance of at least 88% in accordance with the standard         ASTM D1003-97/ISO 13468, and a haze of less than 15%, preferably         less than 10%, preferably less than 5%, in accordance with the         standard ASTM D1003-97, these two properties being measured at         560 nm using a 2 mm thick plate.     -   “antistatic composition” means a composition with a surface         resistivity of less than 10¹² ohm/square measured in accordance         with the standard ASTM D257.

PRIOR ART

The surface of the majority of plastic materials are known to form and retain a static electricity charge. In the case of PMMA, during transport of granules of PMMA in particular, static electricity formation on the PMMA granules means that these granules stick to each other, making them difficult to separate, and they form a block which, for example, makes unloading of the granules problematic. The presence of static electricity on transparent PMMA items may cause dust to accumulate on these items, thus impairing their use and their esthetic appearance. On an industrial scale, residual PMMA powder also has a tendency to stick to machined parts. The accumulation of dust on the surface of these items alters their transparency.

The prior art has described antistatic agents such as ionic surfactants of the ethoxylated amine or sulfonate type which are added to the polymers. However, the antistatic properties of the polymers depend on the ambient humidity and they are not permanent, because these agents migrate to the surface of the polymers and disappear. Thus, copolymers with hydrophilic polyether and polyamide blocks have been proposed; those agents have the advantage of not migrating and thus of providing permanent antistatic properties that, in addition, are independent of the ambient humidity.

Thus, the aim of the present invention is to make transparent PMMA permanently antistatic without altering its transparency.

Japanese patent application JP 60 023 435 A published on 6 Feb. 1985 describes antistatic compositions comprising 5% to 80% of polyetheresteramide and 95% to 20% of a thermoplastic resin selected, inter alia, from polystyrene, ABS and PMMA, that resin being functionalized by acrylic acid or maleic anhydride. Some examples show compositions constituted by 60 to 70 parts of carboxylated PMMA and 40 to 30 parts of polyetheresteramide (per 100 parts). Other examples show compositions consisting of 30 to 45 parts of carboxylated PMMA, 40 to 25 parts of PMMA and 30 parts of polyetheresteramide (per 100 parts). There is no mention of the transparency of PMMA-based compositions, and in addition, it is necessary to provide large quantities of carboxylated PMMA.

Japanese patent application JP 03 237 149 A published on 23 Oct. 1991 describes antistatic compositions consisting of 40% to 99% of an acrylic resin, 1% to 60% of polyetheresteramide and 0.2% to 15% of a grafted polymer having maleic anhydride or epoxy functions and a soluble portion in the acrylic resin. The graft polymer is complicated to prepare.

Japanese patent applications JP 08 253640 A published on 1 Oct. 1996 and JP 04 146 947 A published on 20 May 1992 describe antistatic and transparent compositions constituted by acrylic resin, polyetheresteramide and salts. Adding salts to compositions of this type is not desirable, as they can then migrate during use of the compositions.

Japanese patent applications JP 05 295 213 A published on 9 Nov. 1993 and JP 05 287 157 A published on 2 Nov. 1993 describe antistatic and transparent compositions constituted by acrylic resin, polyetheresteramide and an optional electrolyte or sulfonic acid. They suffer from the same disadvantage as the preceding compositions.

Japanese patent applications JP 05 078 543 A and JP 04 146 947 A describe antistatic and transparent compositions consisting of acrylic resin and polyetheresteramide. The mechanical properties of the basic resin are greatly altered.

Patent application EP 1144505 describes an antistatic composition with an improved impact resistance comprising, per 100 parts by weight: 5 to 20 parts of polyamide block-containing and polyether block-containing copolymer essentially comprising ethylene oxide motifs —(C₂H₄—O)—; and 95 to 80 parts of (A)+(C), (A) being an acrylic polymer, (C) being a polymer selected from acrylic impact modifiers, copolymers (C1) with a low styrene content and an unsaturated carboxylic acid anhydride, copolymers (C2) of ethylene and an unsaturated carboxylic acid anhydride, copolymers (C3) of ethylene and an unsaturated epoxy or mixtures thereof. However, the observed properties in terms of surface resistivity have been shown to be insufficient and the transparency of the PMMA is greatly altered.

Thus, the aim of the present invention is to provide a transparent composition based on PMMA with permanent antistatic properties, which is ready for use and easy to implement, which does not suffer from the disadvantages of the prior art, and which has mechanical properties which are unmodified compared with PMMA.

Novel PMMA compositions have now been discovered that are both permanently antistatic and transparent. The Applicant has demonstrated that, surprisingly, adding a type of block copolymer comprising a total PEG content of more than 50% by weight to a PMMA matrix means that a PMMA can be obtained that has improved antistatic properties which are permanent while retaining the same transparency as the PMMA alone, as well as retaining its mechanical properties.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 represents the log of the surface resistivity for different compositions: 100% PMMA1 or 80% PMMA1/20% PEBA.

FIG. 2 represents the haze (%) as a function of the PEBA content (for PEBA 1 and for PEBA 2) in a composition based on PMMA1.

DETAILED DESCRIPTION OF THE INVENTION

The present invention thus concerns a transparent antistatic composition based on polymethyl methacrylate (PMMA), comprising:

-   -   55% to 99.9% by weight of PMMA, and     -   0.1% to 45% by weight of at least one polyamide (PA)         block-containing and polyether (PE) block-containing copolymer         (PEBA) comprising polyethylene glycol (PEG), with respect to the         total composition weight, said copolymer being characterized in         that it comprises in the range 50% to 80% by weight of PEG with         respect to the total weight of copolymer.

Advantageously, said composition comprises:

-   -   65% to 97%, preferably 70% to 95%, preferably 80% to 93%,         preferably 80% to 88%, preferably 85% to 88% by weight of PMMA,         and     -   3% to 35%, preferably 5% to 30%, preferably 7% to 20%,         preferably 12% to 20%, preferably 12% to 15% by weight of         copolymer comprising PEG,         with respect to the total composition weight.

Preferably, said copolymer comprises 55% to 75%, preferably 60% to 70% by weight of PEG with respect to the total weight of copolymer.

The term “PMMA” denotes a homopolymer or copolymer of methyl methacrylate (MMA) or mixtures thereof.

In one embodiment, the homo- or co-polymer of methyl methacrylate (MMA) comprises at least 70%, preferably at least 80%, advantageously at least 90% and more advantageously at least 95% by weight of methyl methacrylate.

In another embodiment, the PMMA is a mixture of at least one homopolymer and at least one copolymer of MMA, or a mixture of at least two homopolymers or two copolymers of MMA having different molecular weights, or a mixture of at least two MMA copolymers having different monomer compositions.

The methyl methacrylate copolymer (MMA) comprises 70% to 99.7% by weight of methyl methacrylate and 0.3% to 30% by weight of at least one monomer containing at least one ethylenically unsaturated bond which can copolymerize with the methyl methacrylate.

These monomers are well known; particular mention can be made of acrylic and methacrylic acids and alkyl (meth)acrylates in which the alkyl group contains 1 to 12 carbon atoms. By way of example, mention can be made of methyl acrylate and ethyl, butyl or 2-ethylhexyl (meth)acrylate. Preferably, the comonomer is an alkyl acrylate in which the alkyl group contains 1 to 4 carbon atoms.

In a preferred embodiment, the methyl methacrylate copolymer (MMA) comprises 80% to 99.7%, advantageously 90% to 99.7% and more advantageously 90% to 99.5% by weight of methyl methacrylate and 0.3% to 20%, advantageously 0.3% to 10% and more advantageously 0.5% to 10% by weight of at least one monomer containing at least one ethylenically unsaturated bond which can copolymerize with the methyl methacrylate.

Preferably, the comonomer is selected from methyl acrylate or ethyl acrylate or mixtures thereof.

The mass average molecular mass of the (meth)acrylic polymer may be high, which means more than 50 000 g/mol, preferably more than 100 000 g/mol.

The mass average molecular mass may be measured by steric exclusion chromatography (SEC).

Regarding the (meth)acrylic monomer, the monomer is selected from acrylic acid, methacrylic acid, alkyl acrylic monomers, alkyl methacrylic monomers and mixtures thereof.

Preferably, the monomer is selected from acrylic acid, methacrylic acid, alkyl acrylic monomers, alkyl methacrylic monomers and their mixtures, the alkyl group containing 1 to 22 linear, branched or cyclic carbons; the alkyl group preferably contains 1 to 12 linear, branched or cyclic carbons.

Advantageously, the (meth)acrylic monomer is selected from methyl methacrylate, ethyl methacrylate, methyl acrylate, ethyl acrylate, methacrylic acid, acrylic acid, n-butyl acrylate, isobutyl acrylate, n-butyl methacrylate, isobutyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, isobornyl acrylate, isobornyl methacrylate and mixtures thereof.

More advantageously, the (meth)acrylic monomer is selected from methyl methacrylate, isobornyl acrylate or acrylic acid and mixtures thereof.

In a preferred embodiment, at least 50% by weight, preferably at least 60% by weight of the monomer is methyl methacrylate.

In a more preferred embodiment, at least 50% by weight, preferably at least 60% by weight, more preferably at least 70% by weight and advantageously at least 80% by weight and still more advantageously 90% by weight of the monomer is a mixture of methyl methacrylate with isobornyl acrylate and/or acrylic acid.

PMMA additives which may be mentioned are organic additives such as impact strength modifying agents generally known as “impact modifiers”, or sequenced copolymers, thermal stabilizers, UV stabilizers, lubricants and mixtures thereof.

The impact modifier is in the form of fine particles comprising an elastomeric core and at least one thermoplastic envelope, the particle size generally being below 1 μm and advantageously in the range 50 to 300 μm. The impact modifier is prepared by emulsion polymerization. The quantity of impact modifier in the liquid (meth)acrylic syrup is 0 to 50% by weight, preferably 0 to 25% by weight and advantageously 0 to 20% by weight.

PMMA fillers which may be mentioned are carbon nanotubes or mineral fillers, including mineral nanofillers (TiO₂, silica).

The polyether block-containing and polyamide block-containing copolymers, abbreviated to “PEBA”, result from polycondensation of polyamide blocks having reactive ends with polyether blocks having reactive ends such as, inter alia:

1) polyamide blocks having diamine chain ends with polyoxyalkylene blocks having dicarboxylic chain ends. 2) polyamide blocks having dicarboxylic chain ends with polyoxyalkylene blocks having diamine chain ends obtained, for example, by cyanoethylation and hydrogenation of aliphatic dihydroxylated alpha-omega polyoxyalkylene blocks known as polyetherdiols. 3) polyamide blocks having dicarboxylic chain ends with polyetherdiols, the products obtained in this particular case being polyetheresteramides.

The polyamide blocks having dicarboxylic chain ends originate, for example, from the condensation of polyamide precursors in the presence of a chain-limiting dicarboxylic acid. The polyamide blocks having diamine chain ends originate, for example, from the condensation of polyamide precursors in the presence of a chain-limiting diamine.

The number average molar mass Mn of the polyamide blocks is in the range 400 to 20000 g/mole, preferably in the range 500 to 10000 g/mole.

The polyamide block-containing and polyether block-containing polymers may also comprise motifs distributed in a random manner.

Advantageously, three types of polyamide blocks may be used:

-   -   In the first type, the polyamide blocks originate from the         condensation of a dicarboxylic acid, in particular those         containing 4 to 20 carbon atoms, preferably those containing 6         to 18 carbon atoms and an aliphatic or aromatic diamine, in         particular those containing 2 to 20 carbon atoms, preferably         those containing 6 to 14 carbon atoms.

Examples of dicarboxylic acids that may be cited are 1,4-cyclohexyldicarboxylic acid, butanedioic, adipic, azelaic, suberic, sebacic, dodecanedicarboxylic, octadecanedicarboxylic acids and terephthalic and isophthalic acids, but also dimerized fatty acids.

Examples of diamines that may be cited are tetramethylene diamine, hexamethylenediamine, 1,10-decamethylenediamine, dodecamethylenediamine, trimethylhexamethylene diamine, the isomers of bis-(4-aminocyclohexyl)-methane (BACM), bis-(3-methyl-4-aminocyclohexyl)methane (BMACM), and 2-2-bis-(3-methyl-4-aminocyclohexyl)-propane (BMACP), and para-amino-di-cyclo-hexyl-methane (PACM), and isophoronediamine (IPDA), 2,6-bis-(aminomethyl)-norbornane (BAMN) and piperazine (Pip).

Advantageously, blocks PA4.12, PA4.14, PA4.18, PA6.10, PA6.12, PA6.14, PA6.18, PA9.12, PA10.10, PA10.12, PA10.14 and PA10.18 are used.

-   -   In the second type, the polyamide blocks are the result of         condensation of one or more alpha-omega aminocarboxylic acids         and/or one or more lactams containing 6 to 12 carbon atoms in         the presence of a dicarboxylic acid containing 4 to 12 carbon         atoms or a diamine. Examples of lactams that may be cited are         caprolactam, oenantholactam and lauryllactam. Examples of         alpha-omega amino carboxylic acids that may be cited are         aminocaproic, amino-7-heptanoic, amino-11-undecanoic and         amino-12-dodecanoic acids.

Advantageously, the polyamide blocks of the second type are polyamide 11, polyamide 12 or polyamide 6.

-   -   In accordance with a third type, the polyamide blocks result         from the condensation of at least one alpha-omega         aminocarboxylic acid (or a lactam), at least one diamine and at         least one dicarboxylic acid.

In this case, the PA polyamide blocks are prepared by polycondensation:

-   -   of the linear or aromatic aliphatic diamine or diamines         containing X carbon atoms;     -   of the dicarboxylic acid or acids containing Y carbon atoms; and     -   the comonomer or co-monomers {Z}, selected from lactams and         alpha-omega aminocarboxylic acids containing Z carbon atoms and         equimolar mixtures of at least one diamine containing X1 carbon         atoms and at least one dicarboxylic acid containing Y1 carbon         atoms, (X1, Y1) being different from (X, Y),     -   said comonomer or co-monomers {Z} being introduced in a         proportion by weight of up to 50%, preferably up to 20%, still         more advantageously up to 10% with respect to the whole of the         polyamide precursor monomers;     -   in the presence of a chain limiter selected from dicarboxylic         acids.

Advantageously, the chain limiter used is the dicarboxylic acid containing Y carbon atoms, which is introduced in excess with respect to the stoichiometry of the diamine or diamines.

In a variation of this third type, the polyamide blocks result from condensation of at least two alpha-omega aminocarboxylic acids or at least two lactams containing 6 to 12 carbon atoms or a lactam and an aminocarboxylic acid not containing the same number of carbon atoms in the optional presence of a chain limiter. Examples of an aliphatic alpha-omega aminocarboxylic acid that may be cited are aminocaproic, amino-7-heptanoic, amino-11-undecanoic and amino-12-dodecanoic acids. Examples of lactams that may be cited are caprolactam, oenantholactam and lauryllactam. Examples of aliphatic diamines that may be cited are hexamethylenediamine, dodecamethylenediamine and trimethylhexamethylene diamine. An example of a cycloaliphatic diacid that may be cited is 1,4-cyclohexyldicarboxylic acid. Examples of aliphatic diacids that may be cited are butanedioic, adipic, azelaic, suberic, sebacic, dodecanedicarboxylic acids, dimerized fatty acids (these dimerized fatty acids preferably have a dimer content of at least 98%; preferably, they are hydrogenated; they are commercially available under the trade mark “PRIPOL” from “UNICHEMA”, or the trade name EMPOL from HENKEL) and α,ω polyoxyalkylene diacids. Examples of aromatic diacids that may be cited are terephthalic (T) and isophthalic (I) acid. Examples of cycloaliphatic diamines that may be cited are the isomers of bis-(4-aminocyclohexyl)-methane (BACM), bis-(3-methyl-4-aminocyclohexyl)methane (BMACM), and 2-2-bis-(3-methyl-4-aminocyclohexyl)-propane (BMACP), and para-amino-di-cyclo-hexyl-methane (PACM). Other diamines that are frequently used are isophoronediamine (IPDA), 2,6-bis-(aminomethyl)-norbornane (BAMN) and piperazine.

Examples of polyamide blocks of the third type that may be cited are as follows:

-   -   6.6/6, in which 6.6 denotes hexamethylenediamine motifs         condensed with adipic acid. 6 denotes motifs resulting from the         condensation of caprolactam.     -   6.6/6.10/11/12, in which 6.6 denotes hexamethylenediamine         condensed with adipic acid. 6.10 denotes hexamethylenediamine         condensed with sebacic acid. 11 denotes motifs resulting from         the condensation of aminoundecanoic acid. 12 denotes motifs         resulting from the condensation of lauryllactam.

Advantageously, said at least one polyarnide block of the copolymer(s) used in the composition of the invention comprises at least one of the following polyamide monomers: 6, 11, 12, 5.4, 5.9, 5.10, 5.12, 5.13, 5.14, 5.16, 5.18, 5.36, 6.4, 6.9, 6.10, 6.12, 6.13, 6.14, 6.16, 6.18, 6.36, 10.4, 10.9, 10.10, 10.12, 10.13, 10.14, 10.16, 10.18, 10.36, 10.T, 12.4, 12.9, 12.10, 12.12, 12.13, 12.14, 12.16, 12.18, 12.36, 12.T and mixtures or copolymers thereof; and preferably selected from the following polyamide monomers: 6, 11, 12, 6.10, 10.10, 10.12, and their mixtures or copolymers.

Preferably, the PA blocks comprise at least 30%, preferably at least 50%, preferably at least 75%, preferably 100% by weight of PA 11 with respect to the total weight of the PA blocks.

The polyether blocks represent 50% to 80% by weight of the polyamide and polyether block-containing copolymer. The mass Mn of the polyether blocks is in the range 100 to 6 000 g/mole and preferably in the range 200 to 3 000 g/mole.

The polyether blocks are constituted by alkylene oxide motifs. These motifs may usually be ethylene oxide motifs, propylene oxide motifs or tetrahydrofuran (which produces polytetramethylene glycol concatenations). In the present composition of the invention, PEG blocks (polyethylene glycol) are used, i.e. those constituted by ethylene oxide motifs, optionally combined with PPG (propylene glycol) blocks, i.e. those consisting of propylene oxide motifs, PO3G (polytrimethylene glycol) blocks, i.e. those consisting of polytrimethylene ether glycol blocks, and/or PTMG blocks, i.e. those consisting of tetramethylene glycol blocks, also known as polytetrahydrofuran. The PEBA copolymers may comprise several types of polyether in their chain, the co-polyethers possibly being block or random copolymers.

Advantageously, the copolymer of the composition also comprises at least one polyether other than PEG, selected from PTMG, PPG, PO3G and mixtures thereof.

The PEBA used in the composition of the invention comprises more than 50%, preferably more than 55%, or even more than 60% by weight of PEG polyether blocks with respect to the total weight of the PEBA.

It is also possible to use blocks obtained by oxyethylation of bisphenols, such as bisphenol A, for example. These latter products have been described in patent EP613919.

The polyether blocks may also consist of primary ethoxylated amines. Examples of primary ethoxylated amines that may be cited are products with formula:

in which m and n are in the range 1 to 20 and x is in the range 8 to 18. These products are commercially available under the trade mark NORAMOX® from CECA and under the trade mark GENAMIN® from CLARIANT.

The flexible polyether blocks may comprise polyoxyalkylene blocks with NH₂ chain ends, blocks of this type possibly being obtained by cyanoacetylation of aliphatic dihydroxylated alpha-omega polyoxyalkylene blocks termed polyetherdiols. More particularly, it is possible to use Jeffamines (for example Jeffamine® D400, D2000, ED 2003, XTJ 542, commercially available products from Huntsman, also described in patent documents JP2004346274, JP2004352794 and EP1482011).

The polyetherdiol blocks are either used as they are and co-polycondensed with polyamide blocks with carboxylic ends, or they are aminated in order to be transformed into polyether diamines and condensed with polyamide blocks having carboxylic ends. The general two-step method for the preparation of PEBA copolymers with ester bonds between the PA blocks and the PE blocks is known and has been described, for example, in French patent FR2846332. The general method for the preparation of the PEBA copolymers of the invention having amide bonds between the PA blocks and the PE blocks is known and has been described, for example, in European patent EP1482011. The polyether blocks may also be mixed with polyarnicie precursors and a diacid chain limiter in order to make the polyamide block-containing and polyether block-containing polymers having motifs distributed in a random manner (one-step process).

Clearly, the designation PEBA in the present description of the invention refers to PEBAX® sold by Arkema, to Vestamid® sold by Evonik®, to Grilamid® sold by EMS, as well as to Pelestat® type PEBA sold by Sanyo, or to any other PEBA from other suppliers. Advantageously, the PEBA copolymers have PA blocks that are PA 6, PA 11, PA 12, PA 6.12, PA 6.6/6, PA 10.10 and/or PA 6.14, preferably PA 11 and/or PA 12 blocks; and PE blocks that are PEG.

Preferably, the copolymer of the invention comprises at least one PEBA selected from: PA6-PEG, PA11-PEG, PA12-PEG, PA10.10-PEG, PA10.12-PEG, PA6/12-PEG and mixtures thereof; and preferably comprises, or better still is, PA11-PEG.

While the block copolymers described above generally comprise at least one polyamide block and at least one polyether block, it is clear that in fact, the present invention encompasses all alloys of a copolymer comprising two, three, four (or more) different blocks selected from those described in the present description, as long as at least one of these blocks is a polyamide block and that the copolymer comprises more than 50% of PEG.

Advantageously, the copolymer alloy of the invention comprises a segmented block copolymer comprising three different types of blocks (denoted “triblock” in the present description of the invention), which result from the condensation of several of the blocks described above. Said triblock is preferably selected from copolyetheresteramides, copolyetheramideurethanes, in which:

-   -   the percentage by weight of polyamide blocks is more than 10%;     -   the percentage by weight of PEG blocks is more than 50%;         with respect to the total mass of the triblock.

Thus, in accordance with one particular embodiment of the composition of the invention, said copolymer comprising PA blocks and PE blocks is a segmented block copolymer comprising three different types of blocks, said copolymer being selected from copolyetheresteramides and copolyetheramideurethanes.

Advantageously, the copolymer has an inherent viscosity of 2 or less; preferably 1.5 or less; preferably 1.4 or less; preferably 1.3 or less; preferably 1.2 or less. It has been shown that the transparency of the composition is improved (increased transmittance) at lower copolymer viscosities. In the present description, the inherent viscosity is measured at a polymer concentration of 0.5% by weight in solution in metacresol with respect to the total weight of the solution, at 20° C., using an Ubbelohde viscosimeter.

Advantageously, because of its permanent antistatic properties and surface resistivity of less than 10¹² ohm/square, the composition of the invention does not require and therefore does not contain an organic salt.

Nevertheless, it is possible to incorporate an organic salt or an ionic liquid into the composition of the invention, in order to further improve its antistatic performance.

Advantageously, the composition of the invention further comprises 0.1% to 10%, preferably 0.1% to 5% by weight of at least one organic salt in the molten state with respect to the total composition weight.

The organic salts are salts that are consisting of organic cations associated with inorganic or organic anions.

Said at least one organic salt is added in the molten state, i.e. when the organic salt is at a temperature above its fusion temperature. Preferably, said at least one organic salt has a fusion temperature of less than 300° C., preferably less than 200° C., preferably less than 100° C., and thus advantageously constitutes an ionic liquid, preferably below 30° C. The principal properties of ionic liquids are in particular that they are non-volatile (no diffusion into the atmosphere of volatile organic compounds), non-flammable (and thus easy to handle and store), stable at high temperatures (certainly up to 400° C.), are very good conductors, and highly stable as regards water and oxygen.

Advantageously, said at least one organic salt comprises at least one cation comprising at least one of the following molecules: ammonium, sulfonium, pyridinium, pyrrolidinium, imidazolium, imidazolinium, phosphonium, lithium, guanidinium, piperidinium, thiazolium, triazolium, oxazolium, pyrazolium, and mixtures thereof.

Advantageously, said at least one organic salt comprises at least one anion comprising at least one of the following molecules: imides, especially bis(trifluoromethanesulfonyl)imide (abbreviated to NTf2-); borates, especially tetrafluoroborate (abbreviated to BF4-); phosphates, especially hexafluorophosphate (abbreviated to PF6-); phosphinates and phosphonates, especially alkyl-phosphonates; amides, especially dicyanamide (abbreviated to DCA-); aluminates, especially tetrachloroaluminate (AlCl4-), halides (such as bromide, chloride, iodide anions, etc), cyanates, acetates (CH₃COO—), especially trifluoroacetate; sulfonates, especially methanesulfonate (CH₃SO₃—), trifluoromethanesulfonate; sulfates, especially ethyl sulfate, hydrogen sulfate, and mixtures thereof.

The term “organic salt” as used in the context of the invention more particularly means any organic salt that is stable at the temperatures used during synthesis of the block copolymer in accordance with the process of the invention. The skilled person will be able to refer to data sheets for organic salts, which indicate the limiting decomposition temperature for each organic salt.

Examples of organic salts that may be used in the synthesis process of the invention that may in particular be cited are organic salts based on the ammonium cation, based on the imidazolium or imidazolinium cation, based on the pyridinium cation, based on the dihydropyridinium cation, based on the tetrahydropyridinium cation, based on the pyrrolidinium cation, based on the guanidine cation, based on the phosphonium cation.

Organic salts based on the ammonium cation associate, for example:

-   -   a N-trimethyl-N-propylammonium cation with a         bis(trifluoromethanesulfonyl)imide anion;     -   a N-trimethyl-N-butylammonium or N-trimethyl-N-hexylammonium         cation with an anion selected from bromide, tetrafluoroborate,         hexafluorophosphate, bis(trifluoromethanesulfonyl)imide;     -   a N-tributyl-N-methylammonium cation with an iodide,         bis(trifluoromethanesulfonyl)imide or dicyanamide anion;     -   a tetraethylammonium cation with a tetrafluoroborate anion;     -   a (2-hydroxyethyl)trimethylammonium cation with a         dimethylphosphate anion;     -   a di(2-hydroxyethyl)ammonium cation with a trifluoracetate         anion;     -   a N,N-di(2-methoxy)ethylammonium cation with a sulfamate anion;     -   a N,N-dimethyl(2-hydroxyethyl)ammonium cation with a         2-hydroxyacetate or trifluoroacetate anion;     -   a N-ethyl-N,N-dimethyl-2-methoxyethyl ammonium cation with a         bis(trifluoromethylsulfonyl)imide anion;     -   an ethyldimethylpropylammonium cation and a         bis(trifluoromethylsulfonyl)imide anion;     -   a methyltrioctylammonium cation and a         bis(trifluormethylsulfonyl)imide anion;     -   a methyltrioctylammonium cation and a trifluoroacetate or         trifluoromethylsulfonate anion;     -   a tetrabutylammonium cation and a bis(trifluoromethyl         sulfonyl)imide anion;     -   a tetramethylammonium cation and a bis(oxalato(2-))-borate or         tris(pentafluoroethyl)trifluorophosphate anion.

It is also possible to cite organic salts based on imidazole, such as disubstituted imidazoles, monosubstituted imidazoles, trisubstituted imidazoles; in particular those based on the imidazolium cation or the imidazolinium cation.

Examples of organic salts based on imidazolium cations that may be cited include, for example:

-   -   a H-methylimidazolium cation with a chloride anion;     -   a 1-ethyl-3-methylimidazolium cation with a chloride, bromide,         tetrafluoroborate, hexafluorophosphate,         trifluoromethanesulfonate, bis(trifluoromethanesulfonyl)imide,         tetrachloroaluminate, ethyl-phosphonate or methyl-phosphonate,         methanesulfonate, ethyl-sulfate, ethyl-sulfonate anion;     -   a 1-butyl-3-methylimidazolium cation with a chloride, bromide,         tetrafluoroborate, hexafluorophosphate,         trifluoromethanesulfonate, bis(trifluoromethanesulfonyl)imide,         tetrachloroaluminate, acetate, hydrogen sulfate,         trifluoroacetate, methanesulfonate anion;     -   a 1,3-dimethylimidazolium cation with a methyl-phosphonate         anion;     -   a 1-propyl-2,3-dimethylimidazolium cation with a         bis(trifluoromethanesulfonyl)imide anion;     -   a 1-butyl-2,3-dimethylimidazolium cation with a         tetrafluoroborate bis(trifluoromethanesulfonyl)imide anion;     -   a 1-hexyl-3-methylimidazolium cation with a tetrafluoroborate,         hexafluorophosphate, bis(trifluoromethanesulfonyl)imide anion;     -   a 1-octyl-3-methylimidazolium cation with a         bis(trifluoromethanesulfonyl)imide anion;     -   a 1-ethanol-3-methylimidazolium cation with a chloride, bromide,         tetrafluoroborate, hexafluorophosphate,         bis(trifluoromethanesulfonyl)imide, dicyanamide anion.

Examples of organic salts based on the pyridinium cation that may also be cited are: N-butyl-3-methylpyridinium bromide, N-butyl-methyl-4-pyridinium chloride, N-butyl-methyl-4-pyridinium tetrafluoroborate, N-butyl-3-methylpyridinium chloride, N-butyl-3-methylpyridinium dicyanamide, N-butyl-3-methylpyridinium methylsulfate, 1-butyl-3-methylpyridinium tetrafluoroborate, N-butylpyridinium chloride, N-butylpyridinium tetrafluoroborate, N-butylpyridinium trifluoromethylsulfonate, 1-ethyl-3-hydroxymethylpyridinium ethylsulfate, N-hexylpyridinium bis(trifluoromethylsulfonyl)imide, N-hexylpyridinium trifluoromethanesulfonate, N-(3-hydroxypropyl)pyridinium bis(trifluoromethylsulfonyl)imide, N-butyl-3-methylpyridinium trifluoromethanesulfonate, N-butyl-3-methylpyridinium hexafluorophosphate.

Examples of organic salts based on a pyrrolidinium cation that may also be cited are: butyl-1-methyl-1-pyrrolidinium chloride, butyl-1-methyl-pyrrolidinium dicyanamide, butyl-1-methyl-1-pyrrolidinium trifluoromethanesulfonate, butyl-1-methyl-1-pyrrolidinium tris(pentafluoroethyl), 1-butyl-1-methylpyrrolidinium bis[oxalato(2-)]borate, 1-butyl-1-methylpyrrolidinium bis(trifluoromethylsulfonyl)imide, 1-butyl-1-methylpyrrolidinium dicyanamide, 1-butyl-1-methylpyrrolidinium trifluoroacetate, 1-butyl-1-methylpyrrolidinium trifluoromethanesulfonate, butyl-1-methyl-1-pyrrolidinium tris(pentafluoroethyl)trifluorophosphate, 1,1-dimethylpyrrolidinium iodide, 1-(2-ethoxyethyl)-1-methylpyrrolidinium bis(trifluoromethylsulfonyl)imide, 1-hexyl-1-methylpyrrolidinium bis(trifluoromethylsulfonyl)imide, 1-(2-methoxyethyl)-1-methyl pyrrolidinium bis(trifluoromethylsulfonyl)imide, methyl-1-octyl-1-pyrrolidinium chloride, 1-butyl-1-methylpyrrolidinium bromide.

It is also possible to cite organic salts associating:

-   -   a 1-ethyl-1-methylpyrrolidinium cation with a bromide,         tetrafluoroborate, hexafluorophosphate,         trifluoromethanesulfonate anion;     -   a 1-butyl-1-methylpyrrolidinium cation with a chloride, bromide,         tetrafluoroborate, hexafluorophosphate,         trifluoromethanesulfonate, bis(trifluoromethanesulfonyl)imide,         dicyanamide, acetate or hydrogen sulfate anion;     -   a N-propyl-N-methylpyrrolidinium cation with a         bis(trifluoromethanesulfonyl)imide anion;     -   a 1-methyl-1-propylpiperidinium cation with a         bis(trifluoromethanesulfonyl)imide anion;

Further examples of organic salts based on a guanidine cation that may be cited are: guanidine trifluoromethylsulfonate, guanidine tris(pentafluoroethyl)trifluoro phosphate, hexamethylguanidine tris(pentafluoroethyl)trifluorophosphate.

It is also possible to cite organic salts based on a phosphonium cation such as: trihexyl(tetradecyl)phosphonium bis[oxalat(2-)]borate; trihexyl(tetradecyl)phosphonium bis(trifluoromethylsulfonyl)imide; trihexyl(tetradecyl)phosphonium tris(pentafluoroethyl)trifluorophosphate.

The list of organic salts and cations and anions cited above that may be included in the composition of organic salts that may be used in the invention is given solely by way of example; it is neither exhaustive nor limiting. As a consequence, the addition of any other organic salt may of course be envisaged in the process of the invention, as long as the decomposition temperature of the organic salt is higher than the temperatures of the steps of the process of the invention during which the organic salt is present.

Advantageously, the composition of the invention further comprises at least one inorganic salt, i.e. an alkali metal salt or alkaline-earth metal salt; those that may in particular be cited include alkali metal salts such as lithium, sodium, potassium, etc.; and those of alkaline-earths such as magnesium, calcium, etc; with organic acids (mono- or di-carboxylic containing 1 to 12 carbon atoms, for example formic acid, acetic acid, propionic acid, oxalic acid, succinic acid, etc; sulfonic acids containing 1 to 20 carbons, for example methanesulfonic acid, p-toluenesulfonic acid, thiocyanic acid, etc.), or mineral acids (halohydric acids, for example hydrochloric acid, hydrobromic acid, perchloric acid, sulfuric acid, phosphoric acid, etc). The following may be cited: potassium acetate, lithium acetate; lithium chloride, magnesium chloride, calcium chloride, sodium chloride, sodium bromide, potassium bromide, magnesium bromide, lithium bromide, lithium perchlorate, sodium perchlorate or potassium perchlorate, potassium sulfate, potassium phosphate, thiocyanate, and the like.

Of these, halides are preferred, preferably lithium chloride, sodium chloride, potassium chloride, potassium acetates and potassium perchlorates. The quantity of inorganic salt is generally in the range 0.001% to 3%, preferably 0.01% to 2%, with respect to the weight of the composition.

The composition of the invention may also be supplemented with stabilizers, plasticizers, lubricants, natural or organic fillers, colorants, pigments, nacres, antimicrobial agents, flame retardants, antistatic agents, agents modifying the viscosity of the copolymer and/or any other additive or adjuvant already cited and well known to the skilled person in the field of thermoplastic polymers.

Advantageously, said PMMA, said PA blocks and/or said PE blocks of the composition of the invention are obtained at least in part from renewable starting materials.

Advantageously, the composition of the invention comprises a quantity of biocarbon of at least 1%, which corresponds to a ¹⁴C/¹²C isotopic ratio of at least 1.2×10⁻¹⁴. Preferably, said composition comprises a quantity of biocarbon of more than 5%, preferably more than 10%, preferably more than 25%, preferably more than 50%, preferably more than 75%, preferably more than 90%, preferably more than 95%, preferably more than 98%, preferably more than 99%, advantageously substantially equal to 100%.

In accordance with a particularly advantageous embodiment of the present invention, the polyamide blocks and/or the polyether blocks and/or the PMMA are obtained in their entirety from renewable materials.

A material of renewable origin, also known as a biomaterial, is an organic material in which the carbon originates from CO₂ recently fixed (on a human scale) by photosynthesis from the atmosphere. On land, this CO₂ is captured or fixed by plants. At sea, the CO₂ is captured or fixed by bacteria or plankton, proceeding to photosynthesis. A biomaterial (100% natural carbon origin) has a ¹⁴C/¹²C isotopic ratio of more than 10⁻¹², typically of the order of 1.2×10⁻¹², while a fossil material has a zero ratio. In fact, the ¹⁴C isotope is formed in the atmosphere and is then integrated by photosynthesis on a time scale of at most a few tens of years. The half-life of ¹⁴C is 5730 years. Thus, the materials obtained from photosynthesis, namely and generally plants, necessarily contain a maximum amount of ¹⁴C isotope.

The biomaterial or biocarbon content is determined by application of the standards ASTM D 6866 (ASTM D 6866-06) and ASTM D 7026 (ASTM D 7026-04). The standard ASTM D 6866 pertains to “Determining the Biobased Content of Natural Range Materials Using Radiocarbon and Isotope Ratio Mass Spectrometry Analysis”, while the standard ASTM D 7026 pertains to “Sampling and Reporting of Results for Determination of Biobased Content of Materials via Carbon Isotope Analysis”. The second standard refers to the first in its first paragraph.

The first standard describes a test for measuring the ¹⁴C/¹²C ratio of a sample and compares it with the ¹⁴C/¹²C of a reference sample of 100% renewable origin, to produce a relative percentage of C of renewable origin in the sample. The standard is based on the same concepts as ¹⁴C carbon dating, but without applying the dating equations.

The ratio that is then calculated is denoted “pMC” (percent Modern Carbon). If the material to be analyzed is a mixture of biomaterial and fossil material (no radioactive isotope), then the value of pMC obtained is directly correlated with the quantity of biomaterial present in the sample. The reference value used for the ¹⁴C dating is a value dating from the 1950s.

That year was chosen because of the existence of nuclear tests in the atmosphere which had introduced large quantities of isotopes into the atmosphere after this date. The reference 1950 corresponds to a pMC value of 100. Because of the thermonuclear tests, the actual value to use is approximately 107.5 (which corresponds to a correction factor of 0.93). The radioactive carbon signature of a modern plant is thus 107.5. A signature of 54 pMC and 99 pMC thus correspond to a quantity of biomaterial in the sample of 50% and 93% respectively.

The standard ASTM D 6866 proposes three techniques for measuring the quantity of the ¹⁴C isotope:

-   -   LSC (Liquid Scintillation Counting) spectrometry using liquid         scintillation. This technique consists of counting “beta”         particles obtained from the disintegration of ¹⁴C. The beta         radiation obtained from a sample with a known mass (known number         of C atoms) is measured over a certain time. This         “radioactivity” is proportional to the number of atoms of ¹⁴C         which can thus be determined. The ¹⁴C present in the sample         emits β radiation which, in contact with scintillating liquid         (scintillator), gives rise to photons. These photons have         different energies (in the range 0 to 156 keV) and form what is         known as a ¹⁴C spectrum. In two variations of this method, the         analysis is based either on CO₂ which has previously been         produced by the carbon-containing sample in an appropriate         absorbing solution, or on benzene after prior conversion of the         carbon-containing sample into benzene. Thus, the standard ASTM D         6866 provides two methods A and C, based on this LSC method.     -   AMS/IRMS (Accelerated Mass Spectrometry coupled with Isotope         Radio Mass Spectrometry). This technique is based on mass         spectrometry. The sample is reduced to graphite or gaseous CO₂,         and analyzed in a mass spectrometer. This technique uses an         accelerator and a mass spectrometer to separate the ¹⁴C from the         ¹²C ions and thus determine the ratio of the two isotopes.

The compositions in accordance with the invention originate at least in part from biomaterial and thus have a biomaterial content of at least 1%, which corresponds to a ¹⁴C content of at least 1.2×10⁻¹⁴. This content is advantageously higher, in particular up to 100%, which corresponds to a ¹⁴C content of 1.2×10⁻¹². Thus, the alloys of the invention may comprise 100% of biocarbon or, in contrast, may result from a mixture with a fossil origin.

Advantageously, the composition in accordance with the invention further comprises at least one agent improving the surface conductivity selected from: hygroscopic agents; fatty acids; lubricants; metals; metallic films; metallic powders; metallic nanopowders; aluminosilicates; amines such as quaternary amines; esters; fibers; carbon black; carbon fibers; carbon nanotubes; polyethylene glycol; intrinsically conductive polymers such as polyaniline, polythiophene, polypyrrole derivatives; masterbatches; and mixtures thereof. Advantageously, the composition of the invention further comprises at least one additive and/or adjuvant selected from organic or inorganic fillers, reinforcing agents, plasticizers, stabilizers, antioxidants. UV screens, flame retardants, carbon black, carbon nanotubes; mineral or organic colorants, pigments, colorants, unmoulding agents, lubricants, foaming agents, shock resistant agents, shrink resistant agents, flame retardants, nucleating agents, and mixtures thereof.

The present invention also pertains to the use of a composition in accordance with the invention for the manufacture of at least a portion of the following items: an industrial part, an automobile part, a safety accessory, sign, luminous strip, signalling and advertizing panel, display, etching, furniture, shop fitting, decoration, contact ball, dental prosthesis, ophthalmological implant, membrane for hemodialysis, optic fibers, artwork, decoration, sculpture, lenses, in particular camera lenses, disposable camera lenses, printing support, in particular a support for direct printing with UV inks for pictures, photographs, window glass, panoramic roof, vehicle headlights, etc.

The transparent compositions based on PMMA of the invention have definitively improved antistatic properties due to the reduction in surface resistivity provided by incorporating at least one block copolymer in accordance with the invention into at least a portion of a PMMA matrix as defined above. Adding said at least one copolymer to said matrix may be carried out using any of the processes known to the skilled person in the field of polymers, in particular by dry mixing, or by mixing at a temperature which is higher than the glass transition temperature of the various added polymers, or by shearing at a temperature substantially equal to the fluidization temperature of the various added polymers, in particular by rolling, extrusion, or by mixing in solution.

Examples

The examples below illustrate the present invention without limiting its scope. In the examples, all of the percentages are percentages by weight unless indicated otherwise.

Products Used in the Examples:

PEBA, not in Accordance with the Invention:

PEBA 1: PA12-PEG with PA12 blocks with a number average molar mass of 1500 g/mol and PEG blocks with a number average molar mass of 1500 g/mol, and inherent viscosity: 1.4.

PEBA 1b, “b” for “low viscosity”: PA12-PEG with PA12 blocks with a number average molar mass of 1500 g/mol and PEG blocks with a number average molar mass of 1500 g/mol, and inherent viscosity: 1.1.

PEBA in Accordance with the Invention:

PEBA 2: PA11-PEG with PA11 blocks with a number average molar mass of 1000 g/mol and PEG blocks with a number average molar mass of 1500 g/mol, and inherent viscosity: 1.4.

PEBA 2b, “b” for “low viscosity”: PA11-PEG with PA11 blocks with a number average molar mass of 1000 g/mol and PEG blocks with a number average molar mass of 1500 g/mol, and inherent viscosity: 1.2.

PMMA:

PMMA1 characterized by an MFI=2 g/10 min (230° C., 3.8 kg) and a Charpy (notched) impact strength at +23° C. of 2 kJ/m².

PMMA2 characterized by an MFI=14.5 g/10 min (230° C., 3.8 kg) and a Charpy (notched) impact strength at +23° C. of 2 kJ/m².

PMMA3 containing an acrylic impact modifier, characterized by an MFI=0.8 g/10 min (230° C., 3.8 kg) and a Charpy (notched) impact strength at +23° C. of kJ/m².

TABLE 1 Trans- mittance Haze (ASTM (ASTM Quantity D1003) D1003) Sample of Pebax (%) (%) 100% PEBA 1 100%  81 61 PEBA PEBA 2 100%  75 74 PEBA 2b 100%  81.7 46 PMMA/ PMMA3 100%  0% 93 0.4 PEBA PMMA3/PEBA 2 (93/7)  7% 91.6 2 compo- PMMA3/PEBA 2 (90/10) 10% 91.1 2.1 sitions PMMA3/PEBA 2 (88/12) 12% 90.4 2.2 (weight PMMA3/PEBA 2 (85/15) 15% 89.5 2.7 ratio) PMMA3/PEBA 2 (80/20) 20% 89.2 3.1 PMMA3/PEBA 2b (93/7)  7% 91.8 2.2 PMMA3/PEBA 2b (90/10) 10% 91.8 2.2 PMMA3/PEBA 2b (88/12) 12% 91.2 3 PMMA3/PEBA 2b (85/15) 15% 91 3.77 PMMA3/PEBA 2b (80/20) 20% 90.1 5.12 PMMA1/PEBA 2 (80/20) 20% 88.4 2.92 PMMA1/PEBA 2b (80/20) 20% 90 5.5 PMMA1/PEBA 1 (80/20) 20% 86.4 15.3 PMMA1/PEBA 1b (80/20) 20% 86.2 25.2 PMMA2/PEBA 2 (80/20) 20% 89.3 4.06 PMMA2/PEBA 2b (80/20) 20% 90.9 5.48 PMMA2/PEBA 1 (80/20) 20% 87.9 19.6 PMMA2/PEBA 1b (80/20) 20% 87.4 25.3

FIG. 1 (or graph 1) represents the log of the surface resistivity for different compositions: 100% PMMA1 or 80% PMMA1/20% PEBA.

The surface resistivity of the PMMA matrix was reduced by at least two powers of ten by incorporating 20% by weight of block copolymer (PEBA) with respect to the total composition weight.

FIG. 2 (or graph 2) represents the haze (%) as a function of the PEBA content (for PEBA 1 and for PEBA 2) in a composition based on PMMA1.

The haze remained less than 4% in the case of compositions of PMMA in accordance with the invention (comprising PEBA2), in contrast to compositions not in accordance with the invention comprising PEBA1. 

1. A transparent antistatic composition based on polymethyl methacrylate (PMMA), comprising: 55% to 99.9% by weight of PMMA, and 0.1% to 45% by weight of at least one polyamide (PA) block-containing and polyether (PE) block-containing copolymer (PEBA) comprising polyethylene glycol (PEG), with respect to the total composition weight, wherein said copolymer comprises in the range between 50% to 80% by weight of PEG with respect to the total weight of copolymer.
 2. The composition as claimed in claim 1, comprising: 65% to 97% by weight of PMMA, and 3% to 35% by weight of copolymer comprising PEG, with respect to the total composition weight.
 3. The composition as claimed in claim 1, in which said copolymer comprises 55% to 75% by weight of PEG with respect to the total weight of copolymer.
 4. The composition as claimed in claim 1, in which said at least one polyamide block comprises at least one of the following polyamide monomers: 6, 11, 12, 5.4, 5.9, 5.10, 5.12, 5.13, 5.14, 5.16, 5.18, 5.36, 6.4, 6.9, 6.10, 6.12, 6.13, 6.14, 6.16, 6.18, 6.36, 10.4, 10.9, 10.10, 10.12, 10.13, 10.14, 10.16, 10.18, 10.36, 10.T, 12.4, 12.9, 12.10, 12.12, 12.13, 12.14, 12.16, 12.18, 12.36, 12.T and mixtures thereof or copolymers.
 5. The composition as claimed in claim 1, in which the PA blocks comprise at least 30% by weight of PA 11 with respect to the total weight of PA blocks.
 6. The composition as claimed in claim 1, in which said copolymer further comprises at least one polyether other than PEG selected from PTMG, PPG, PO3G, and mixtures thereof.
 7. The composition as claimed in claim 1, in which said copolymer comprises at least one PEBA selected from: PA6-PEG, PA11-PEG, PA12-PEG, PA10.10-PEG, PA10.12-PEG and mixtures thereof.
 8. The composition as claimed in claim 1, in which said copolymer comprising PA blocks and PE blocks is a segmented block copolymer comprising three different types of blocks, said copolymer being selected from copolyetheresteramides and copolyetheramideurethanes.
 9. The composition as claimed in claim 1, in which said copolymer has an inherent viscosity of 2 or less.
 10. The composition as claimed in claim 1, in which said PMMA, said PA blocks and/or said PE blocks are obtained at least in part from renewable starting materials.
 11. The composition as claimed in claim 10, comprising a quantity of biocarbon of at least 1%, which corresponds to a ¹⁴C/¹²C isotopic ratio of at least 1.2×10⁻¹⁴.
 12. The composition as claimed in claim 11, comprising a quantity of biocarbon of more than 5%.
 13. The composition as claimed in claim 1, comprising no organic salt.
 14. The composition as claimed in claim 1, further comprising 0.1% to 10% by weight of at least one organic salt in the molten state with respect to the total composition weight.
 15. The composition as claimed in claim 6, in which said at least one organic salt comprises at least one cation comprising at least one of the following molecules: ammonium, sulfonium, pyridinium, pyrrolidinium, imidazolium, imidazolinium, phosphonium, lithium, guanidinium, piperidinium, thiazolium, triazolium, oxazolium, pyrazolium, and mixtures thereof.
 16. The composition as claimed in any one of claim 6, in which said at least one organic salt comprises at least one anion comprising at least one of the following molecules: imides; borates; phosphates; phosphinates and phosphonates; amides; aluminates, halides; cyanates; acetates; sulfonates, trifluoromethanesulfonate; sulfates.
 17. The composition as claimed in claim 1, further comprising at least one agent improving the surface conductivity selected from: hygroscopic agents; fatty acids; lubricants; metals; metallic films; metallic powders; metallic nanopowders; aluminosilicates; amines; esters; fibers; carbon black; carbon fibers; carbon nanotubes; polyethylene glycol; intrinsically conductive polymers; masterbatches; and mixtures thereof.
 18. The composition as claimed in claim 1, further comprising at least one additive and/or adjuvant selected from organic or inorganic fillers, reinforcing agents, plasticizers, stabilizers, antioxidants, UV screens, flame retardants, carbon black, carbon nanotubes; mineral or organic colorants, pigments, colorants, unmoulding agents, lubricants, foaming agents, shock resistant agents, shrink resistant agents, flame retardants, nucleating agents, and mixtures thereof.
 19. A method of using a composition as claimed in claim 1, for the manufacture of at least a portion of the following items: an industrial part, an automobile part, a safety accessory, sign, luminous strip, signalling and advertizing panel, display, etching, furniture, shop fitting, decoration, contact ball, dental prosthesis, ophthalmological implant, membrane for hemodialysis, optic fibers, artwork, sculpture, camera lenses, disposable camera lenses, printing support, in particular a support for direct printing with UV inks for pictures, photographs, window glass, panoramic roof. 